Carvacrol (CV) and carvacryl acetate (CVA) are bioactive compounds that have anthelmintic action and the nanoencapsulation may be an alternative to potentialize their efficacy. The aim of this work was to nanoencapsulate CV and CVA using chitosan/gums and evaluate cytotoxicity and the anthelmintic activity. A 24 factorial experimental design was performed to determine the influence of gum type (arabic or chichá), amount of surfactant and the number of layers in the nanoencapsulation degree. CVA and CV presented encapsulation efficiency (EE) optimum values of 90 and 20% (experiments 8 and 9), respectively. The monolayer and bilayer formulations presented maximum size of 479 and 811 nm, respectively. Nanoencapsulated CVA (nCVA) with bilayer coating and higher surfactant levels showed good thermal stability and no toxicity. In vitro kinetics for nCVA with chitosan/chichá gum showed slower release profiles than nCVA with chitosan/gum arabic, with 50% release after 30 and 20 h, respectively. CVA and nCVA at a concentration of 150 µg mL−1 reduced the motility of H. contortus adult nematodes by 100 and 91.7%, respectively. In summary, nCVA chitosan/chichá gum showed high encapsulation efficiency, favorable release rate and anthelmintic activity against H. contortus.

Nanoparticulas de quitosana (CH) e goma do angico (AG), dopadas com óleo essencial de Lippia sidoides (Ls) foram preparadas e caracterizadas em relação às suas composições, distribuição de tamanho de partículas, estabilidade térmica, bem como as liberações in vitro e in vivo. Os dados obtidos revelaram que as nanopartículas preparadas usando razões Ls:AG variando de 1:2 a 1:20, apresentaram dopagens na faixa de 3,3 a 7,7%, com eficiência de encapsulação entre 16,0 e 77,8%. Os tamanhos de partículas ficaram na faixa de 10-60 nm, com distribuições independentes do teor de óleo incorporado. FTIR revelou a presença de timol, principal componente de Ls. Análises de TGA e DSC mostraram que a incorporação de óleo na matriz resulta em nanopartículas de menor estabilidade térmica. A amostra Ls: AG = 1:10 apresentou um perfil de liberação in vitro mais lento que as demais, exibindo, porém, nos bioensaios, uma maior mortalidade larval.

Chitosan (CH) and angico gum (AG) nanoparticles were loaded with essential oil, Lippia sidoides (Ls), being characterized according to their composition, size distribution, Ls:polymer ratio, thermal stability and in vitro and in vivo controlled release. Nanoparticles prepared using Ls:AG ratios of 1:2 to 1:20 had loading values of 3.3 to 7.7%, with encapsulation efficiencies in the range of 16.0 to 77.8%. Particle sizes were in the range of 10-60 nm and size distributions were independent of Ls content, for different Ls:AG ratios. Infrared spectroscopy revealed the presence of thymol in the nanoparticles. TGA and DSC revealed that the degradation temperature of AG-CH nanoparticles decreased with an increase in Ls content. Controlled-release data showed a slower release profile for samples with Ls:AG = 1:10 than for the other samples. Bioassays showed that sample Ls:AG = 1:10 has a greater larvicidal effect, with 85 ± 3% mortality.

Blendas de polipropileno e elastômeros termoplásticos (TPEs), estireno-b-butadieno-b-estireno (SBS) e estireno-b-etileno-co-butileno-b-estireno(SEBS) foram preparadas com o objetivo de avaliar a influência do tipo e da concentração do elastômero nas propriedades mecânicas e na morfologia das blendas. Foram utilizados dois tipos de polipropileno, um homopolímero de propileno (PP-H) e um copolímero randômico de propileno-etileno (PP-R), sendo avaliado também o efeito das características da matriz termoplástica. O elastômero termoplástico aumentou a resistência ao impacto do PP, e a variação da rigidez das blendas foi dependente somente da quantidade de TPE adicionada, sendo estas comparativamente mais rígidas que aquelas com igual teor de elastômero convencional, tipo EPDM e EPR. A blenda com melhor balanço rigidez-impacto foi aquela de PP-R com 10% de SEBS. As blendas do copolímero de propileno-etileno com os TPEs apresentaram maior deformação do que aquelas com o homopolímero, devido à natureza menos cristalina da matriz do copolímero de propileno. As blendas tanto do homo quanto do copolímero de propileno com SEBS ficaram mais homogêneas em função da maior afinidade do bloco central poliolefínico EB (etileno-co-butileno) do primeiro com a região amorfa da matriz, sendo esta mais significativa no PP-R.

Blends of polypropylene and thermoplastic elastomers (TPEs) of styrene-butadiene-styrene (SBS) and styrene-ethylene-co-butene-styrene (SEBS) triblock copolymers were prepared to evaluate the effect of the elastomer and its concentration on the material properties. For this purpose, a polypropylene homopolymer (PP-H) and a propylene-ethylene random copolymer (PP-R) were used to evaluate the matrix effect on the tensile properties and morphology of the blends. The addition of TPEs to PP promotes increase on impact resistance and the PP-R/SEBS 10%wt blend showed the best balance in stiffness-impact resistance. The morphology of binary blends was similar to elastomeric domains dispersed into the PP matrix and changed as the TPE type and concentration varied. The size of SEBS domains was more homogeneous than the SBS' in both PP matrices due to the high affinity between the polyolefinic EB (ethylene-butene) middle block of the SEBS with the PP amorphous fraction.